Arc Light Electric Welding Electrode
HTJ422 is in line with GB/T 5117 E4303 Equivalent to JIS Z3211 D4303
Description: HTJ422 is a kind of carbon steel welding electrode with titanium-calcium coating, endowed with good welding performance, stable arc, aesthetic appearance and little splash, and suitable for both AC and DC and all-position welding.
Application: Applicable to welding common carbon steel structure and low alloy steel with low strength grade. Such as 09Mn2。
Chemical Composition of Deposited Metal(%)
Item |
C |
Si |
Mn |
P |
S |
Guaranteed Value |
—— |
—— |
—— |
0.040 |
≤0.035 |
Mechanical Properties of Deposited Metal
Performance |
Yield Strength(MPa) |
Tensile Strength |
Elongation |
AKV Impact Value |
|
Guaranteed Value |
≥420 |
≥330 |
≥22 |
0℃ |
≥27 |
HTJ427 is in line with GB/T 5117 E4315
Description: HTJ427 is a kind of carbon steel covered welding electrode with low hydrogen-potassium coating, adopts DC power supply to conduct all-position welding. Weld metal is excellent in mechanical property and crack resistance.
Application: Applicable to welding important carbon steel and low alloy steel.
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
S | P | Cr | Ni | Mo | V |
Guarantee Value |
—— |
≤1.25 |
≤0.90 |
≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
Mechanical Properties of Deposited Metal
Performance |
Yield Strength (MPa) |
Tensile Strength |
Elongation |
AKV Impact Value |
|
Guarantee Value |
≥330 |
≥420 |
≥22 |
-30℃ |
≥27 |
HTJ502 is in line with GB/T 5117 E5003 Equivalent to JIS Z3211 D5003
Description: HTJ502 is a kind of carbon steel welding electrode with titanium-calcium coating, and suitable for both DC and AC and all-position welding.
Application: Applicable to welding of 16Mn and other low alloy steel structure.
Chemical Composition of Deposited Metal(%)
Item |
C |
Si |
Mn |
P |
S |
Guarantee Value |
—— |
—— |
—— |
≤0.040 |
≤0.035 |
Mechanical Properties of Deposited Metal
Performance |
Yield Strength (MPa) |
Tensile Strength |
Elongation |
AKV Impact Value |
|
Guarantee Value |
≥400 |
≥490 |
≥20 |
0℃ |
≥27 |
Description: HTJ506 is a kind of carbon steel covered welding electrode with low hydrogen-potassium coating, and endowed with good welding performance, stable arc, aesthetic appearance, little splash, great slag detachability and good performance of full-position welding. Weld metal is good in plasticity, low temperature toughness and crack resistance.
Application: Applicable to welding of carbon steel structure, low alloy steel (such as, 16Mn, 09Mn2Si, etc.), Grade A, B, D, E marine steel, and important structure of vehicles, buildings, bridges, etc.
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
S | P | Cr | Ni | Mo | V |
Guarantee Value |
—— |
≤1.60 |
≤0.75 |
≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
Mechanical Properties of Deposited Metal
Performance |
Yield Strength (MPa) |
Tensile Strength |
Elongation |
AKV Impact Value |
|
Guarantee Value |
≥400 |
≥490 |
≥22 |
-30℃ |
≥27 |
HTJ507 is in line with GB/T 5117 E5015 Equivalent to AWS A5.1 E7015
Description: HTJ507 is a kind of carbon steel welding electrode with low hydrogen-potassium coating, and a digestive product of international advanced technology. Weld metal is good in plasticity, low temperature toughness and crack resistance. The welding electrode, adopting unique black coating, is endowed with good welding performance, good arc stiffness, little magnetic blow, aesthetic appearance, little splash, good slag detachability and stable arc.
Application: Applicable to welding of carbon steel, low alloy steel (such as, 16Mn, etc.), Grade A, B, D, E marine steel and important steel structures of boilers, pressure containers and pipes, etc.
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
S | P | Cr | Ni | Mo | V |
Guarantee Value |
—— |
≤1.60 |
≤0.75 |
≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
Mechanical Properties of Deposited Metal
Performance |
Tensile Strength |
Elongation |
Guarantee Value |
≥490 |
≥22 |
HTJ501Fe16 is in line with GB/T 5117 E5024 Equivalent to AWS A5.1 E7024
Description: TJ501Fe16 is a kind of iron powder-titanium coated electrode, suitable for DC/AC power source, and downward weld and flat fillet weld, with the nominal efficiency of 160%.
Application: Applicable to welding of carbon steel, low alloy steel (such as, 16Mn, etc.) and structures of ships, vehicles, and machines.
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
S | P | Cr | Ni | Mo | V |
Guarantee Value |
—— |
≤1.25 |
≤0.90 |
≤0.035 | ≤0.040 | ≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
Mechanical Properties of Deposited Metal
Performance |
Yield Strength (MPa) |
Tensile Strength |
Elongation |
Guarantee Value |
≥400 |
≥490 |
≥17 |
HTA002 is in line with GB/T 983 E308L-16 and equivalent to AWS A5.4 E308L-16
Description: HTA002 is a kind of the extra-low-carbon stainless steel welding electrode with titanium-calcium coating; the metal content of its weld metal is less than 0.04%; it is great in intercrystalline corrosion resistance and AC arc stability and suitable for both AC and DC.
Application: Applicable to welding 00Cr19Ni10 extra-low-carbon steel structure and 0Cr18Ni10Ti corrosion-resistant stainless steel structures at the working temperature lower than 300℃.
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
Cr | Ni | Cu | Mo | S | P |
Guarantee Value |
≤0.04 |
0.5-2.5 |
≤0.90 |
18.0-21.0 | 9.0-11.0 | ≤0.75 | ≤0.75 | ≤0.30 | ≤0.040 |
Mechanical Properties of Deposited Metal
Performance |
Tensile Strength(MPa) |
Elongation(%) |
Guarantee Value |
≥520 |
≥35 |
HTA022 is in line with GB/T 983 E316L-16 Equivalent to AWS A5.4 E316L-16
Description: HTA022 is a kind of extra-low-carbon stainless steel electrode with titanium-calcium coating and suitable for both AC and DC power source. Its weld metal has good heat resistance, corrosive resistance and crack resistance, and welding performance.
Application: Applicable to welding of carbamide and synthetic fiber equipments and similar stainless steel structures as well as Cr stainless steel, compound steel and profiled steel that can not be subjected to heat treatment after welding.
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
S | P | Cr | Ni | Mo | Cu |
Guarantee Value |
≤0.04 |
0.5-2.5 |
≤0.90 |
≤0.30 | ≤0.040 | 17.0-20.0 | 11.0-14.0 | 2.0-3.0 | ≤0.75 |
Mechanical Properties of Deposited Metal
Performance |
Tensile Strength |
Elongation |
Guarantee Value |
≥420 |
≥30 |
HTA102 is in line with GB/T 983 E308-16 Equivalent to AWS A5.4 E308-16
Description: HTA102 is a kind of stainless steel electrode with titanium-calcium coating, suitable for both DC and AC power source, and with good resistance to intergranular corrosion and AC arc stability.
Application: Applicable to welding 0Cr18Ni9 corrosion-resistant stainless steel structure with work temperature below 300℃.
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
S | P | Cr | Ni | Mo | Cu |
Guarantee Value |
≤0.08 |
0.5-2.5 |
≤0.90 |
≤0.30 | ≤0.040 | 18.0-21.0 | 9.0-11.0 | ≤0.75 | ≤0.75 |
Mechanical Properties of Deposited Metal
Performance |
Tensile Strength |
Elongation |
Guarantee Value |
≥550 |
≥35 |
HTA202 is in line with GB/T 983 E316-16 Equivalent to AWS A5.4 E316-16
Description: HTA202 is a kind of stainless steel electrode with titanium-calcium coating and its weld metal is good in corrosive resistance, heat resistance and crack resistance, and especially useful to resist chloride ion corrosive pitting. Suitable for both AC and DC, it is endowed with good welding performance and especially suitable for downward welding and fillet welding of thin plates.
Application: Applicable to welding 0Cr18Ni12Mo2 stainless steel equipments working in organic / inorganic acid (non-oxidation acid) media, and high Cr steel and profiled steel that can not be subjected to heat treatment after welding.
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
S | P | Cr | Ni | Mo | Cu |
Guarantee Value |
≤0.08 |
0.5-2.5 |
≤0.90 |
≤0.030 | ≤0.040 | 17.0-20.0 | 11.0-14.0 | 2.0-3.0 | ≤0.75 |
Mechanical Properties of Deposited Metal
Performance |
Tensile Strength |
Elongation |
Guarantee Value |
≥520 |
≥30 |
HTA062 is in line with GB/T 983 E309L-16 Equivalent to AWS A5.4 E309L-16
Description: HTA602 is a kind of extra-low-carbon nuclear power steel welding electrode with titanium-calcium coating, suitable for AC/DC power source, and endowed with the advantages of good welding performance, little splash, stable arc and aesthetic appearance. Because of low carbon content, it can resist the intergranular corrosion caused by carbide precipitation without Nb and Ti and other stabilizers.
Application: Applicable to welding nuclear power projects, such as pressure containers and related structures.
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
S | P | Cr | Ni |
Guarantee Value |
—— |
≤1.60 |
≤0.75 |
≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
Mechanical Properties of Deposited Metal
Performance |
Tensile Strength |
Elongation |
Guarantee Value |
565 |
42.0 |
HTA302 is in line with GB/T 983 E309-16 Equivalent to AWS A5.4 E309-16 JB/T4747 E309-16
Description: HTA302 is a kind of stainless steel electrode with low titanium-calcium coating and special for pressure container, suitable for both AC and DC and endowed with good welding performance. Its weld metal has good crack resistance and oxidation resistance.
Application: Applicable to welding stainless steel similar to pressure window, stainless steel linings, profiled steel (Cr19Ni10 and low carbon steel)
Chemical Composition of Deposited Metal(%)
Item | C |
Mn |
Si |
S | P | Cr | Ni | Mo | Cu |
Guarantee Value |
≤0.15 |
0.5-2.5 |
≤0.90 |
≤0.030 | ≤0.035 | 22.0-25.0 | 12.0-14.0 | ≤0.75 | ≤0.75 |
Mechanical Properties of Deposited Metal
Performance |
Tensile Strength |
Elongation |
Guarantee Value |
≥550 |
≥25 |